发布日期：2019-7-20 16:32:38
1、高精度钛棒的公差：
| 基本尺寸 （直径，mm） | h | ||||||||
| 5 | 6 | 7 | 8 | 9 | 10 | 11 | 12 | ||
| 大于 | 至 | 偏差mm | |||||||
| - | 3 | 0 -0.004 | 0 -0.006 | 0 -0.010 | 0 -0.014 | 0 -0.025 | 0 -0.04 | 0 -0.060 | 0 -0.10 |
| 3 | 6 | 0 -0.005 | 0 -0.008 | 0 -0.012 | 0 -0.018 | 0 -0.03 | 0 -0.048 | 0 -0.075 | 0 -0.12 |
| 6 | 10 | 0 -0.006 | 0 -0.009 | 0 -0.015 | 0 -0.022 | 0 -0.036 | 0 -0.058 | 0 -0.09 | 0 -0.15 |
| 10 | 18 | 0 -0.008 | 0 -0.011 | 0 -0.018 | 0 -0.027 | 0 -0.043 | 0 -0.070 | 0 -0.110 | 0 -0.18 |
| 18 | 30 | 0 -0.009 | 0 -0.013 | 0 -0.021 | 0 -0.033 | 0 -0.052 | 0 -0.084 | 0 -0.130 | 0 -0.21 |
| 30 | 50 | 0 -0.011 | 0 -0.016 | 0 -0.025 | 0 -0.039 | 0 -0.062 | 0 -0.100 | 0 -0.160 | 0 -0.25 |
| 50 | 80 | 0 -0.013 | 0 -0.019 | 0 -0.030 | 0 -0.046 | 0 -0.074 | 0 -0.120 | 0 -0.190 | 0 -0.30 |
| 80 | 120 | 0 -0.015 | 0 -0.022 | 0 -0.035 | 0 -0.054 | 0 -0.087 | 0 -0.140 | 0 -0.220 | 0 -0.35 |
2、高精度钛棒的直线度、椭圆度：
科辉钛业生产的高精度钛棒直线度可达到0.3/1000mm,椭圆度0.006mm
3、医用钛棒的力学性能指标：
1>GB/T 13810-2007
| TC4 | ||||
| 直径 （mm） | 抗拉强度 MPa | 屈服强度 MPa | 伸长率 % | 断面收缩率 % |
| >1.0-2.0 | >925 | >8 | ||
| >2.0-7.0 | >895 | >10 | ||
| >7-50 | >930 | >860 | >10 | >25 |
| >50-90 | >895 | >830 | >10 | >25 |
| TC4ELI | ||||
| >1-7.0 | >860 | >10 | ||
| >7-45 | >860 | >795 | >10 | >25 |
| >45-65 | >825 | >760 | >8 | >20 |
| >65-90 | >825 | >760 | >8 | >15 |
2>ASTM F136
| Ti6Al4VELI | ||||
| 直径 （mm） | 抗拉强度 MPa | 屈服强度 MPa | 伸长率 % | 断面收缩率 % |
| <4.75 | >860 | >795 | >10 | |
| >4.75-44.45 | >860 | >795 | >10 | >25 |
| >44.45-63.5 | >825 | >760 | >8 | >20 |
| >63.5-101.6 | >825 | >760 | >8 | >15 |
3>ISO 5832-3
| Ti6Al4V | ||||
| 直径 （mm） | 抗拉强度 MPa | 屈服强度 MPa | 伸长率 % | 断面收缩率 % |
| >1.0-75 | >860 | >780 | >10 | |